LOW DENSITY POLYETHYLENE

LOW DENSITY POLYETHYLENE

PROPERTY

PHYSICAL	METHOD	CONDITION	UNIT	VALUE
Melt Index	ASTM D1238	190‘Ι/2.16kg	g/10min	3
Melting Temperature	DSC	10‘Ι/min	‘Ι	110
Density	ASTM D792	23‘Ι	g/cm³	0.921
THERMAL	METHOD	CONDITION	UNIT	VALUE
Vicat Softening Poin	ASTM D1525	1kg	‘Ι	90

FILM CHARATERISTICS

CHARATERISTICS	METHOD	CONDITION	UNIT	VALUE
Tensile Strength at Yield	ASTM D882	TD	kg/cm² MPa psi	190 18.8 2701.8
Tensile Strength at Break	ASTM D882	MD	kg/cm² MPa psi	185 18.3 2630.7
Tensile Strength at Yield	ASTM D882	TD	kg/cm² MPa psi	610 60.2 8674.2
Elongation at Break	ASTM D882	MD	%	610
Elongation at Break	ASTM D882	TD	%	420
Tear Strength	ASTM D1922	MD	g	350
Tear Strength	ASTM D1922	TD	g	300
Dart Impact Resistance	ASTM D1709	-	g	110
Slip cofficient	ASTM D1894	-	-	0.08
Water Vapor Permeability	House	-	g/cm²·24hrs	10.5
Oxygen Permeability	House	-	g/cm²·24hrs	2000
Nitrogen Permeability	House	-	g/cm²·24hrs	7500
Haze	ASTM D1003	-	%	8

COMMENTS

Packing : 25kgs in bag

SUPPLIERS
Korea	Daelim Industrial Co., Ltd. www.daelimchem.co.kr
Korea	Hanwha Chemical Corp. http://hcc.hanwha.co.kr
Korea	LG Chem Ltd www.lgchem.com
Korea	SK Corporation www.skcorp.com